Luvocom® 3F PAHT 9936 BK Filament.
A high-temperature PA6 with mineral filler, black, made for mechanical strength that goes past conventional filaments. It also insulates exceptionally well and resists oils, and common FFF printers should handle it, direct drive as well as Bowden. read further
- Excellent electrical insulation
- Continuous service at 120 °C
- Resists oils and lubricants
For custom specs, technical validation, or bulk pricing. Speak with an engineer before you order.
Freshly produced on demand and typically shipped within 3 working days.
Luvocom 3F PAHT 9936: a mineral-filled nylon that insulates.
| Property | Condition | Value | Test method |
|---|---|---|---|
| Specific gravity | 1,25 g/cm³ | ISO 1183-3 | |
| Water absorption | 23°C / 24h | <0,3 % | ISO 62 |
| Melt flow rates (MFR) | 250°C / 2,16kg | 5,5 g/10 min | ISO 1133 |
| Melt volume rate (MVR) | 250°C / 2,16kg | 5 cm³/10 min | ISO 1133 |
| Linear mould shrinkage | 0,3-0,5 % | DIN 16742 |
| Property | Condition | Value | Test method |
|---|---|---|---|
| Tensile strength | dry, @50 mm/min | 78 MPa | ISO 527 |
| Elongation at maximum force | dry, @50 mm/min | 4,4 % | ISO 527 |
| Modulus of elasticity | dry, @1 mm/min | 3,4 GPa | ISO 527 |
| Charpy impact strength | dry | 90 kJ/m² | ISO 179 1eU |
| Property | Condition | Value | Test method |
|---|---|---|---|
| Heat distortion temperature | HDT A | 90 °C | ISO 75 |
| Continuous service temperature | 20.000 h | 120 °C | IEC 60216 |
| Service temperature | during lifetime max. 200h | 160 °C |
| Property | Condition | Value | Test method |
|---|---|---|---|
| Insulation resistance strip electrode R25 | >10¹² Ω | DIN IEC 60167 | |
| Surface resistance | ROB | >10¹² Ω | DIN IEC 60093 |
An industrial polyamide with a drying step you cannot skip.
| Parameter | Value |
|---|---|
| Nozzle temperature | 265 to 290 °C |
| Heated bed temperature | above 50 °C |
| Print speed | 40 to 60 mm/s |
| Adhesion | Magigoo PA on a CF plate, glass or a PEI sheet |
| Drying | 100 °C, 4 to 6 hours or 80 °C, 12 hours |
| Layer thickness | 0.2 mm or thicker |
| Nozzle | Abrasion resistant |
| Filament weight | Spool | Empty weight |
|---|---|---|
| 500 to 750 g | RS 200 GH2L PC | 243 g |
| 1000 g | RS 200 KDL PC | 256 g |
Precision-engineered consistency.
Consistent prints start with a uniform filament shape. We continuously monitor diameter and roundness during production. When filament varies in size or loses its round profile, material flow becomes erratic. This causes under-extrusion and weak layer bonds.
Our manufacturing process keeps the cross-section stable across the full spool. Your printer receives a steady volume of material without pressure drops in the nozzle. You get predictable extrusion on every job, so with Luvocom® 3F PAHT 9936 BK you can focus on your design, not your material.
Sealed at the source. Never touched by water.*
Unlike manufacturers who cool filament in a water bath, our filament never touches water during production. Moisture inside the material creates bubbles and weakens layer bonding during printing. Water-free production keeps extrusion consistent and bubble-free.
Sealed and ready to print.
We produce on demand. Every spool is vacuum-sealed immediately after extrusion, so it reaches you dry. This process keeps every spool of Luvocom® 3F PAHT 9936 BK ready to print out of the box.
* At times of high demand, and for some variants, production may run on a conventional water-cooled line. Contact us before ordering if you require material produced with our water-free process.
Vacuum-sealed on the production line, before it ever leaves the machine.
Precision you can track. From pellet to part.
We produce every spool on demand in our own facility. This gives us direct oversight that mass-produced stock lacks. Your spool comes from a fresh, identifiable batch rather than long-term warehouse inventory. We document the production trail for every run.
Documented, not just shipped.
We keep the production logs for every batch we make. On request, we link a Certificate of Analysis and Technical Data Sheet to your specific batch. You get clear data for your spool of Luvocom® 3F PAHT 9936 BK.
Dutch engineering for parts that define the future.
At 3D4M, we develop and manufacture high-performance thermoplastic filaments for demanding applications across aerospace, defence, semiconductor, automotive, medical research, and industrial manufacturing. We work with engineers, researchers, and manufacturers who need materials that go beyond standard specifications.
Our engineering starts with the machines themselves. We design and build our own extrusion lines around our patented extrusion process, combining material expertise with technology developed in-house. For moisture-sensitive polymers, our air-cooling technology offers a water-free cooling option, allowing us to tailor the production process to the material.
Our production facility is built on a single, uncompromising principle: control. From our extrusion technology to precise diameter monitoring and vacuum-sealed packaging, we control every stage to deliver consistent filament with batch traceability.
Trusted by global leaders
Supporting over 100 universities alongside global industry leaders, we have become a trusted partner to advanced research labs and manufacturers worldwide. We bring together material expertise and Dutch engineering to help turn ambitious ideas into reliable, high-performance parts.
3D4M headquarters, Haarlem, the Netherlands.
Validating this material for your application?
The leap to a high-performance polymer can be complex. Speak directly with one of our material engineers about your printer setup, target specifications, and material performance. We are here to help you de-risk your validation phase.
Specify your specs. We'll start your batch.
Experience the benefits of freshly extruded, water-free filament. Select your required diameter and spool weight in the order panel to initiate our on-demand production process. We ship worldwide, vacuum-sealed and ready.
Place your order